High Tensile Galvanized Baling Wire for Pulp and Cotton Packaging (2.0–4.0 mm)
- Diameter range: 2.0 mm – 4.0 mm
- Common sizes: 2.3 mm and 3.0 mm
- Zinc coating: 210–275 g/m²
- Tensile strength: 950–2150 MPa depending on diameter
- Packing: Coil/Spool, 300–1000 kg per unit
Made to order to your diameter, coating, tensile grade and standard — request a quote for price, minimum order quantity and lead time.
Specifications
| Dia. Range (mm) | Tensile (MPa) |
| Elongation (%) | Zinc Coating (g/m²) |
| 1.58–2.0 | 1100–1550 |
| 2.0–3.05 | 1280–1410 |
| 4 | 220–230 |
| 3.05–3.6 | 1280–1410 |
| 4 | 240 |
| 3.6–4.0 | 1240–1380 |
Tensile Strength
Tensile strength ranges from 950 MPa to 2150 MPa depending on diameter and zinc coating. Elongation ≥ 4%.
Features
- Available in 2.0–4.0 mm for baling use
- Common sizes: 2.3 mm and 3.0 mm
- High zinc coating ensures excellent corrosion resistance
- Used in cotton baling, pulp packing, and recycling
- Produced to ASTM B498, ASTM A475, JIS G 3537, and B957 standards
Packaging & Shipping
Packing: 300–1000 kg per coil or spool
Packaging Options: Wrapped with plastic film and gunny cloth
Delivery Time: 15–30 working days
Export Options: Sea freight, truck freight, or customized solutions
Use cases
- Baling and unitizing wire for pulp, paper and cotton bales
- Black-annealed binding and tying wire for packaging
- Bright and galvanized packing wire for recycling and industrial bundling
Who it is for
Pulp, paper, recycling and packaging producers running manual, semi-automatic or automatic balers.
Standards, certificates & inspection
Produced to your tensile, diameter and finish specification, with a mill test certificate per batch. Every batch is produced under an ISO 9001 quality management system and can ship with a mill test certificate covering diameter, tensile strength and zinc-coating weight. Third-party or pre-shipment inspection (SGS, BV or customer-appointed) is available on request.
See test reports & inspection and quality control & testing for the full documentation.
Frequently asked questions
What is this baling wire for?
High-tensile galvanized wire for pulp and cotton bale packaging on baling and strapping presses.
How does it differ from unitizing wire?
Both bale product, but our unitizing wire targets a defined 965–1172 MPa window; here 2.0–4.0 mm and tensile are confirmed to your press.
Which related packaging wires do you offer?
Bright galvanized unitizing wire, black annealed packing wire and flat packing/stitching wire.
Request a quote
Send your diameter, coating, standard and quantity, and we’ll reply with a quotation.
Get a QuoteTechnical documents
Download the product catalogue, or contact us for certificates and test reports.
Product catalogue (PDF)You May Also Need
Bright Galvanized Unitizing Wire for Pulp Bale Strapping (2.2–3.0 mm, 965–1172 MPa)
- Diameter range: 2.2–3.0 mm
- Tensile strength: 965–1172 MPa
- Bright galvanized coating: ~55 g/m²
Black Annealed Low Carbon Wire for Packing, Tying and General Fabrication (1.6–12.5 mm)
- Diameter range: 1.6 mm – 12.5 mm
- Tensile strength range: 500–1100 MPa depending on diameter
- Made from low carbon steel with heat treatment and annealing
Flat Steel Wire for Packing, Stitching and Industrial Use
- Special rectangular section — specified by width × thickness and an approved drawing, never as a diameter
- Controlled edge/corner radius, camber and twist for machine feed and forming
- Mechanical grade selected for forming or stiffness; tensile confirmed after flattening